| The following specifications have been provided by the manufacturer. This table is provided for as suggestions for preliminary design. Final application and design should be verified by a professional prior to final specification or construction. |  |
||
 |
| Properties - Polypropylene | Test
Method ASTM or GRI |
fPP 30 mil |
fPP 40 mil |
fPP-R 36 mil |
fPP-R 45 mil |
Testing
Frequency Minimum |
| Mass per Unit Area - lb/ft (min.ave.) | D5261 |
0.12 |
0.16 |
0.15 |
0.18 |
15,000
lb |
| Thickness
- Mils (min.ave.) Lowest individual specimen - mils, nominal-10% |
D5199 |
30 |
40 36 |
36 32 |
45 40 |
roll |
| Tensile
Strength Dumbell (1) - lb/in. (min.ave.) Grab (1) - lb (min.ave.) |
D638-IV D751-A |
60 -- |
72 -- |
-- 200 |
-- 250 |
15,000 lb 15,000 lb |
| Tensile
Elongation Dumbell (1,2) - % (min.ave.) grab (1) - % (min.ave.) |
D638-IV D751-A |
700 -- |
700 -- |
-- 22 |
-- 22 |
15,000 lb 15,000 lb |
| Multiaxial Elongation | D-5617 |
120 |
120 |
-- |
-- |
formulation |
| Tear
Resistance nonreinforced (1)-lb(min.ave.) reinforced (1)-lb(min.ave.) |
D1004 D5884 |
10 -- |
12 -- |
|
-- 55 |
15,000 lb 15,000 lb |
| Puncture Resistance - lb (min.ave.) | D4833
|
25
|
30
|
75
|
85
|
15,000
lb
|
| Ply Adhesion lb (min.ave.) | D6636
|
--
|
--
|
15
|
15
|
15,000
lb
|
| Low Temperature Flexibility - °F | D2136 (3) |
-40 |
-40 |
-40 |
-40 |
formulation |
| Carbon Black Content (4) - % | D4218 |
2-3 |
2-3 |
2-3 |
2-3 |
45,000
lb |
Oven
Aging at 85°C (6) |
D5721 D5885
|
Black
fPP & fPP-R 60
|
Other
Colors
fPP & fPP-R 50
|
formulation |
||
| Ultraviolet
Light Resistance (6,7) (a) Standard OIT (min.ave.) - % ret. After 1600 hrs. -or- (b) High Pressure OIT (min.ave.) - % ret. After 1600 hrs. -and- (c) Surface Cracking Observation |
GM11 D5885
|
80
|
60
|
formulation | ||
| (1) Test methods modified to 20 in./min. for unreinforced and 12 in./min. for reinforced. | ||
| (2) Calculation based on a 2.0 in. gage length | ||
| (3) Using 1/ in. mandrel for 4-hours | ||
| (4) Applicable only to black geomembranes. Also D1603 is an acceptable
method to determine carbon black content. |
||
| (5) Not recommended since high temperature of the Std-OIT test procedures an unrealistic result for some antioxidants used in fPP formulations. | ||
| (6) It is also recommended to evaluate samples at 15 days to compare with the 30 day response. | ||
| (7) The condition of the test should be 20 hr. UV cycle at 75ºC followed by 4 hr. condensation at 60ºC.` | ||
| All values are nominal test results, except when specified as minimum or maximum. These specifications are offered as an informational guide for consideration to assist project coordinators with their specifications. These values are not intended as a warranty or guarantee, and Colorado Lining International assumes no liability in connection with this information. Colorado Lining International reserves the right to change specifications contained herein without notice. | ||
|
|
|
||
| THE COMPANY. . . . . | who
we are 
offices
contacts
events
our people
privacy policy
terms of use |
|
| PRODUCTS . . . . . . . | pvc
hypalon
epdm
hdpe
rpp
specialty
products
|
|
| APPLICATIONS . . . | recreation
agriculture
environment
industry
municipal
decorative
floating
covers |
|
|
WeatherBeater athletic field covers
project
profiles photo
gallery |
||
| SERVICES . . . . . . . . | consulting
design
fabrication
installation
guarantee
partnering
request
more information |
|
| affiliates | ||
| AIDS . . . . . | home
site
map help
glossary
faqs
request
assistance |
|
|
|
||
|
Copyright
© 1997-2005 Colorado Lining International, Inc. All Rights
Reserved. |
||
| Last modified on 6-25-04 |